REGULARITIES OF THE FORMATION OF SURFACE CRACKS IN CYLINDRICAL LOGS

The article considers the regularities of formation of surface cracks in cylindrical logs. The production of these logs is a promising and useful because of useful output in their production is up to 80% and provide supportive and comfortable. We found that the lack of these logs are shrinkage and surface cracks generated during operation after installation is not dried logs in the logs. It is shown that cracks impair the appearance and durability of wooden houses due to the wicking in them of atmospheric moisture. It is proved that the cracking is due to uneven-dimensional drying of outer and inner layers of logs. Set numerical values of the stresses over the cross section of logs. It is proved that the drying of the outer and inner layers of logs through the early drilled longitudinal hole technology will eliminate the formation of surface cracks in cylindrical logs.

Keywords: logs, surface cracks, drying, stress

В статье рассмотрены закономерности образования поверхностных трещин в оцилиндрованных бревнах. Производство этих бревен перспективно и целесообразно, т.к. полезный выход при их изготовлении составляет до 80% и обеспечиваются благоприятные и комфортные условия проживания. Выявлено, что недостатком этих бревен являются усадка и поверхностные трещины, образующиеся в процессе эксплуатации после установки не высушенных бревен в сруб. Показано, что трещины ухудшают внешний вид и продолжительность срока службы деревянных домов из-за затекания в них атмосферной влаги. Доказано, что появление трещин связано с неравномерной сушкой наружных и внутренних слоев бревен. Установлены численные значения напряжений по сечению бревен. Обосновано, что сушка наружных и внутренних слоев бревен через раннее высверленное продольное технологическое отверстие устранит образование поверхностных трещин в оцилиндрованных бревнах.

Ключевые слова: оцилиндрованное бревно, поверхностные трещины, сушка, напряжения